Titanium Beta-C

printer-friendly version - back to material properties chart

General Information
Material		Material Properties			Maximum Working Temp.	Ultimate Tensile Range (ksi min)	Modulus of Elasticity	Approx. Design % of Ultimate Tensile (torsional)	Common Sizes (inches)
Titanium Beta-C AMS 4957 UNS R58640		Age hardened. Good ductility and toughness. Good fabricability, and good resistance to general corrosion. Good for environments containing Ferric Chloride, Sodium Chloride, Carbon Dioxide, and Hydrogen Sulfide.			600°F	190/180	(E)15.4 (G)5.9	45%	.005" to .625"
Wire Sizes (Diameter in Inches)
.005	.007	.008	.009	.010	.012	.014	.015	.017	.018
.021	.022	.025	.032	.045	.048	.050	.054	.062	.072
.080	.093	.105	.114	.125	.135	.148	.156	.162	.177
.187	.192	.207	.225	.243	.250	.312	.343	.375	.406
.437	.500	.562	.625
Tensile Strength
Diameter inches (mm)				Minimum Tensile Strength psi (MPa)		Maximum Tensile Strength psi (MPa)		Minimum Elongation in 2 inches (50 mm)
Up to 0.187 (4.75)				190,000 (1310)		210,000 (1450)		10%
Over 0.187 (4.75) to 0.375 (9.53)				185,000 (1275)		205,000 (1415)		10%
Over 0.375 (9.53) to 0.625 (15.88)				180,000 (1240)		200,000 (1380)		8%

Comments
Material has been cold drawn 20 - 35% final reduction. Additional cold reduction may be possible to produce higher tensile/yield strength. Larger sizes can be obtained in spring tempered and annealed condition. Check with a Suhm representative for further information.

This data is provided as a reference guide only and is not intended for design purposes. Strength values and sizes are subject to change. Please check with a Suhm Spring representative for confirmation.