Inconel X-750 Bar

printer-friendly version - back to material properties chart

General Information
Material		Material Properties			Maximum Working Temp.	Ultimate Tensile Range (ksi min)	Modulus of Elasticity	Approx. Design % of Ultimate Tensile (torsional)	Common Sizes (inches)
Inconel X-750 Bar ASTM B637 UNS N07500		Cold drawn. Good corrosion resistance. Good for use in elevated temperature applications. Good for use in Sour-Gas applications.			700°F	170	(E)29 (G)11.2	45%	.750" to 2.500"
Wire Sizes (Diameter in Inches)
.750	.812	.956	.968	1.000	1.125	1.150	1.187	1.312	1.325
1.375	1.500	1.625	1.750	2.125	2.250	2.500
Tensile and Hardness Requirements
Alloy	Heat Treatment		Minimum Tensile Strength psi (MPa)		Minimum Yield Strength (0.2% offset) psi (MPa)		Reduction of Area Minimum %		Brinell Hardness
N07750 Type 2^c	solution at 1800°F (982°C) + precipitation harden		170,000 (1170)		115,000 (790)		18%		302 to 363

Comments
Material is produced in either the solution annealed or solution annealed/aged condition. This specification only requires that minimum strength values be met. Aging time and temperatures are extensive (20 Hrs. @ 1300°F) to produce the required strengths. Bar lengths, in general, will average 12’ to 14’; however, Suhm maintains a stocking arrangement to have available 10’ - 20’ lengths on some sizes. Some sizes are available in lengths up to 35'. Check with a Suhm representative for further information.

This data is provided as a reference guide only and is not intended for design purposes. Strength values and sizes are subject to change. Please check with a Suhm Spring representative for confirmation.